40/50 Bitumen
Definition:
It is a kind of bitumen, which is provided during the process of oxidation of vacuum bottom (the bitumen production feedstock that derives from distillation tower residue in vacuum oil refineries) at bitumen production units. In a manner that its penetration point (kind of test to indicate the hardness of bitumen) becomes between 40-50.
Characteristics:
Bitumen 40/50 |
|
Specification |
Test method |
Specific gravity @25/25 C |
1.01-1.06 |
D-70 |
Penetration @25 C |
40/50 |
D-5 |
Softening point C |
52/60 |
D-36 |
Ductility @25 C |
100 min |
D-113 |
Loss on heating (wt)% |
0.2 max |
D-6 |
Drop in penetration after heating % |
20 max |
D-6 & D-5 |
Flash point C |
250min |
D-92 |
Solubility in CS2 (wt)% |
99.5 min |
D-4 |
Spot test |
negative |
*A.A.S.H.O.T.102 |
60/70 Bitumen
Definition:
It is a kind of bitumen, which is provided during the process of oxidation of vacuum bottom (the bitumen production feedstock that derives from distillation tower residue in vacuum oil refineries) at bitumen production units. In a manner that its penetration point (kind of test to indicate the hardness of bitumen) becomes between 60-70.
Characteristics:
Bitumen 60/70 |
|
Specification |
Test method |
Specific gravity @25/25 C |
1.01-1.06 |
D-70 |
Penetration @25 C |
60/70 |
D-5 |
Softening point C |
49/56 |
D-36 |
Ductility @25 C |
100 min |
D-113 |
Loss on heating (wt)% |
0.2 max |
D-6 |
Drop in penetration after heating % |
20 max |
D-6 & D-5 |
Flash point C |
250min |
D-92 |
Solubility in CS2 (wt)% |
99.5 min |
D-4 |
Spot test |
negative |
*A.A.S.H.O.T.102 |
85/100 Bitumen
Definition:
It`s kind of bitumen which is provided during the process of oxidation of vacuum bottom (the bitumen production feedstock that derives from distillation tower residue in vacuum oil refineries) at bitumen production units. In which its penetration point (kind of test to indicate the hardness of bitumen) becomes between 85-100.
Characteristics:
Bitumen 85/100 |
|
Specification |
Test method |
Specific gravity @25/25 C |
1.01-1.05 |
D-70 |
Penetration @25 C |
85/100 |
D-5 |
Softening point C |
45/52 |
D-36 |
Ductility @25 C |
100 min |
D-113 |
Loss on heating (wt)% |
0.5 max |
D-6 |
Drop in penetration after heating % |
20 max |
D-6 & D-5 |
Flash point C |
232 max |
D-92 |
Solubility in CS2 (wt)% |
99.5 min |
D-4 |
Organic matter insoluble in CS2 (wt)% |
0.2 max |
D-4 |
Spot test |
negative |
*A.A.S.H.O.T.102 |
Flash Point C |
232min |
D-92 |
|
232min |
|
85/25 Bitumen
Definition:
at the bitumen production reactor, during the air acting, the mixture of the two Vacuum Bottom (VB) and Vacuum Silabes (VS) feedstock is put under a special degree of pressure and temperature between 200-300°C of which the hydrogen atoms content in bitumen molecular oxidize to oxygen of air, and obtains with higher hydrocarbons polymerization reaction that has lower penetration and higher softening points than the primary pure bitumen. This kind of bitumen has the softening point of 85 and permeability of 25.
Characteristics:
Bitumen R85/25 |
|
Specification |
Test method |
Specific gravity @25/25 C |
1.05 approx |
D-70 |
Penetration @25 C |
20/30 |
D-5 |
Softening point C |
80/90 |
D-36 |
Ductility @25 C |
3 min |
D-113 |
Loss on heating (wt)% |
0.2 max |
D-6 |
Flash point C |
225 max |
D-92 |
Solubility in CS2 (wt)% |
99 min |
D-4 |
90/15 Bitumen
Definition :
at the bitumen production reactor, during the air acting, the mixture of the two Vacuum Bottom (VB) and Vacuum Silabes (VS) feedstock pressed under a special and temperature pressure between 200-300°C of which the hydrogen atoms content in bitumen molecular oxidize to oxygen of air, and obtains with higher hydrocarbons polymerization reaction that has lower penetration and bigger softening points rather than the primary pure bitumen. This kind of bitumen has the softening point of 90 and permeability of 15.
Characteristics:
Bitumen R90/15 |
|
Specification |
Test method |
Specific gravity @25/25 C |
1.05 approx |
D-70 |
Penetration @25 C |
10/20 |
D-5 |
Softening point C |
85/95 |
D-36 |
Ductility @25 C |
1.5 min |
D-113 |
Loss on heating (wt)% |
0.2 max |
D-6 |
Flash point C |
225 max |
D-92 |
Solubility in CS2 (wt)% |
99 min |
D-4 |
|